条款 | 测试要求 | 测试标准 |
1. 板材测试项目 | ||
1 | 面积重 | ASTM D5947-06 |
2 | 密度 | ASTM D792-08(Immersion Method) |
ASTM C271-2005 | ||
3 | 热变形温度 | ASTM D648-07 |
4 | 弯曲强度 | ASTM D790-07e1 |
5 | 弯曲模量 | ASTM D790-07e1 |
6 | 穿孔剪切强度 | ASTM D732-10 |
7 | 剥离强度 | ASTM D903-98(2004) |
ASTM D1781-98(2004) | ||
8 | 拉伸强度 | ASTM D638-10 |
ASTM E8/E8M-09 | ||
9 | 屈服抗拉强度 | ASTM D638-10 |
ASTM E8/E8M-09 | ||
10 | 弯曲剪切强度 | ASTM C393/C393M-06 |
11 | 平面拉伸强度 | ASTM C297/C297M-04 |
12 | 拉伸剪切强度 | ASTM C273/C273M-07a |
13 | 拉伸剪切模量 | |
14 | 平压强度 | ASTM C365/C365M-05 |
15 | 平压模量 | |
16 | 侧压强度 | ASTM C364/C364M-07 |
2.涂层测试项目 | ||
1 | 漆膜厚度 | ASTM D7091-05 |
ISO 2360-2003(涡流法) | ||
2 | 镜面光泽度 | ASTM D523-08 |
ASTM D5767-95(2004) | ||
ISO 2813-1994/Cor 1:1997 | ||
3 | 漆膜附着力(划格法) | ASTM D3359-09 |
ISO 2409-2007 | ||
4 | 铅笔硬度 | ASTM D3363-05 |
ISO 15184-1998 | ||
5 | 柔韧性 | ASTM D522-93a(2008) (Mandrel bend) |
ASTM D4145-10 (T bend) | ||
6 | 杯突 | ISO 1520-2006 |
7 | 刮花 | ISO 1518-1992 |
8 | 耐冲击 | ASTM D2794-93(2010) |
9 | 落砂磨耗 | ASTM D968-05e1 Method A |
10 | 耐清洁剂 | ASTM D2248-01a(2007) |
11 | 耐化学试剂 | ASTM D1308-02(2007) |
12 | 耐泥浆性 | ASTM C207-06 |
AAMA 2605-05 铝型材和板材上的超高性能有机涂层的推荐规范、性能要求和测试方法 | ||
条款 | 测试要求 | 测试标准 |
1 | 色彩均匀性 | AAMA 2605-05 Section 7.1 ASTM D2244-07e1 |
2 | 60℃镜面光泽度 | AAMA 2605-05 Section 7.2 ASTM D523-08 |
3 | 干膜硬度 | AAMA 2605-05 Section 7.3 ASTM D3363 |
4 | 涂层干式附着力 | AAMA 2605-05 Section 7.4.1.1 |
5 | 涂层湿式附着力 (24h浸水,38°C) | AAMA 2605-05 Section 7.4.1.2 |
6 | 涂层沸水煮附着力 | AAMA 2605-05 Section 7.4.1.3 |
7 | 耐冲击测试 | AAMA 2605-05 Section 7.5 |
8 | 耐落沙磨耗 | AAMA 2605-05 Section 7.6 ASTM D968-05e1 |
9 | 耐盐酸 (15 mins,10%HCl) | AAMA 2605-05 Section 7.7.1 |
10 | 耐泥浆 (24h, 100% RH,38°C) | AAMA 2605-05 Section 7.7.2 |
11 | 耐硝酸(30 mins) | AAMA 2605-05 Section 7.7.3 |
12 | 耐清洁剂(72h, 38°C) | AAMA 2605-05 Section 7.7.4 |
13 | 耐窗户清洗剂 | AAMA 2605-05 Section 7.7.5 |
14 | 耐湿 (4000h,100% RH,38°C) | AAMA 2605-05 Section 7.8.1 ASTM D2247-02 or ASTM D4585-07 |
15 | 耐盐雾(4000h) | AAMA 2605-05 Section 7.8.2 ASTM B117-07a |
16 | 耐候 (南佛罗里达州,北纬27度,45度角面向南方,最少10年曝晒) | AAMA 2605-05 Section 7.9 |
颜色保持力 | ASTM D2244 Section 6.3 | |
耐粉化性 | ASTM D4214 | |
光泽度保持力 | ASTM D523 | |
耐侵蚀 | ASTM B244 | |
AAMA 2604-05 铝型材和板材上的高性能有机涂层的推荐规范、性能要求和测试方法 | ||
条款 | 测试要求 | 测试标准 |
1 | 色彩均匀性 | AAMA 2604-05 Section 7.1 ASTM D2244-07e1 |
2 | 60℃镜面光泽度 | AAMA 2604-05 Section 7.2 ASTM D523-08 |
3 | 干膜硬度 | AAMA 2604-05 Section 7.3 ASTM D3363 |
4 | 涂层干式附着力 | AAMA 2604-05 Section 7.4.1.1 |
5 | 涂层湿式附着力(24h浸水,38°C) | AAMA 2604-05 Section 7.4.1.2 |
6 | 涂层沸水煮附着力 | AAMA 2604-05 Section 7.4.1.3 |
7 | 耐冲击测试 | AAMA 2604-05 Section 7.5 |
8 | 耐落沙磨耗 | AAMA 2604-05 Section 7.6 ASTM D968-05e1 |
9 | 耐盐酸 (15 mins,10%HCl) | AAMA 2604-05 Section 7.7.1 |
10 | 耐泥浆 (24h, 100% RH,38°C) | AAMA 2604-05 Section 7.7.2 |
11 | 耐硝酸(30 mins) | AAMA 2604-05 Section 7.7.3 |
12 | 耐清洁剂 (72h, 38°C) | AAMA 2604-05 Section 7.7.4 |
13 | 耐窗户清洗剂 | AAMA 2604-05 Section 7.7.5 |
14 | 耐湿(3000h,100% RH,38°C) | AAMA 2604-05 Section 7.8.1 ASTM D2247-02 or ASTM D4585-07 |
15 | 耐盐雾 (3000h) | AAMA 2604-05 Section 7.8.2 ASTM B117-07a |
16 | 耐候 (南佛罗里达州,北纬27度,45度角面向南方,最少5年曝晒) | AAMA 2604-05 Section 7.9 |
颜色保持力 | ASTM D2244 Section 6.3 | |
耐粉化性 | ASTM D4214 | |
光泽度保持力 | ASTM D523 | |
耐侵蚀 | ASTM B244 | |
AAMA 2603-02 铝型材和板材上的着色有机涂层的推荐规范、性能要求和测试方法 | ||
条款 | 测试要求 | 测试标准 |
1 | 色彩均匀性 | AAMA 2603-02 Section 6.1 ASTM D2244-07e1 |
2 | 60℃镜面光泽度 | AAMA 2603-02 Section 6.2 ASTM D523-08 |
3 | 干膜硬度 | AAMA 2603-02 Section 6.3 ASTM D3363 |
4 | 涂层干式附着力 | AAMA 2603-02 Section 6.4.1.1 |
5 | 涂层湿式附着力 (24h浸水,38°C) | AAMA 2603-02 Section 6.4.1.2 |
6 | 耐冲击测试 | AAMA 2603-02 Section 6.5 |
7 | 耐盐酸(15 mins,10%HCl) | AAMA 2603-02 Section 6.6.1 |
8 | 耐泥浆(24h, 100% RH,38°C) | AAMA 2603-02 Section 6.6.2 |
9 | 耐清洁剂(72h, 38°C) | AAMA 2603-02 Section 6.6.3 |
10 | 耐湿 (1500h,100% RH,38°C) | AAMA 2603-02 Section 6.7.1 ASTM D2247-02 or ASTM D4585-07 |
11 | 耐盐雾 (1500h) | AAMA 2603-02 Section 6.7.2 ASTM B117-07a |
12 | 耐候 (南佛罗里达州,45度角面向南方,1年曝晒) | AAMA 2603-02 Section 6.8 |
颜色保持力 | ASTM D2244 Section 6.3 | |
耐粉化性 | ASTM D4214 | |
光泽度保持力 | ASTM D523 | |
耐侵蚀 | ASTM B244 | |
AAMA 611-98 阳极氧化建筑用铝非官方技术规范 | ||
条款 | 测试要求 | 测试标准 |
1 | 氧化层厚度 | AAMA 611-98 Section 9.1 ASTM B244 or ASTM B487 |
2 | 氧化层重量和表观密度 | AAMA 611-98 Section 9.2 ASTM B137 |
3 | 色彩均匀性 | AAMA 611-98 Section 9.3 AATCC 173 |
4 | 60℃镜面光泽度 | AAMA 611-98 Section 9.4 ASTM D523-08 |
5 | 磨耗测试 (Michael Clark Abrasion Test) | AAMA 611-98 Section 9.5 |
6 | 耐腐蚀测试(盐雾腐蚀) | AAMA 611-98 Section 9.6 ASTM B117 |
7 | 耐候测试 (南佛罗里达州,北纬27度,45度角面向南方,5年曝晒) | AAMA 611-98 Section 9.7 |
颜色保持力 | ASTM D2244 Section 6.3 | |
耐粉化性 | ASTM D4214 | |
光泽度保持力 | ASTM D523 | |
耐侵蚀 | ASTM B244 | |
8 | 密封测试 | AAMA 611-98 Section 9.8 ASTM B680 or ISO 3210 |
9 | 裂纹测试 | AAMA 611-98 Section 9.9 |
AAMA 612-02 Voluntary Specification, Performance Repuirements, and Test Procedures for Combined Coatings of Anodic Oxide and Transparent Organic Coating on Architectural Aluminum AAMA 612-02 建筑用铝阳极氧化与透明有机复合涂层的推荐规范、性能要求和测试方法 |
||
条款 | 测试要求 | 测试标准 |
1 | 复合涂层厚度 | AAMA 612-02 Section 7.1 ASTM B244 |
2 | 氧化层重量和表观密度 | AAMA 612-02 Section 7.2 ASTM B137 |
3 | 色彩均匀性 | AAMA 612-02 Section 7.3 AATCC 173 |
4 | 60℃镜面光泽度 | AAMA 612-02 Section 7.4 ASTM D523 |
5 | 有机涂层硬度 | AAMA 612-02 Section 7.5 ASTM D3363 |
6 | 涂层干式附着力 | AAMA 612-02 Section 7.6.1.1 |
7 | 涂层湿式附着力(24h浸水,38°C) | AAMA 612-02 Section 7.6.1.2 |
8 | 涂层沸水煮附着力 (20 mins, 99~100°C) | AAMA 612-02 Section 7.6.1.3 |
9 | 耐冲击测试 | AAMA 612-02 Section 7.7 |
10 | 耐落沙磨耗 | AAMA 612-02 Section 7.8 ASTM D968 |
11 | 耐盐酸 | AAMA 612-02 Section 7.9.1 |
12 | 耐泥浆 | AAMA 612-02 Section 7.9.2 |
13 | 耐硝酸 | AAMA 612-02 Section 7.9.3 ASTM D2244 |
14 | 耐清洁剂 | AAMA 612-02 Section 7.9.4 |
15 | 耐窗户清洗剂 | AAMA 612-02 Section 7.9.5 |
16 | 耐湿 (4000h,100% RH,38°C) | AAMA 612-02 Section 7.10.1 ASTM D2247 or ASTM D4585 |
17 | 耐盐雾 (4000h) | AAMA 612-02 Section 7.10.2 ASTM B117 |
18 | 裂纹测试 | AAMA 612-02 Section 7.11 |
19 | 耐候测试 (南佛罗里达州,北纬27度,45度角面向南方,5年曝晒) | AAMA 612-02 Section 7.12 |
颜色保持力 | AAMA 612-02 Section 7.12.1.2 ASTM D2244 Section 6.3 | |
耐粉化性 | AAMA 612-02 Section 7.12.1.3 ASTM D4214 | |
光泽度保持力 | AAMA 612-02 Section 7.12.1.4 ASTM D523 | |
耐侵蚀 | AAMA 612-02 Section 7.12.1.5 ASTM B244 | |
AAMA 620-02 滚涂结构铝底层的高性能有机涂层的规范 | ||
条款 | 测试要求 | 测试标准 |
1 | 色彩均匀性 | AAMA 620-02 Section 7.1 ASTM D2244 |
2 | 60℃镜面光泽度 | AAMA 620-02 Section 7.2 ASTM D523 |
3 | 干膜硬度 | AAMA 620-02 Section 7.3 ASTM D3363 |
4 | 涂层干式附着力 | AAMA 620-02 Section 7.4.1.1 |
5 | 涂层湿式附着力(24h,38°C) | AAMA 620-02 Section 7.4.1.2 |
6 | 涂层沸水煮附着力 | AAMA 620-02 Section 7.4.1.3 |
7 | 耐背面冲击测试 | AAMA 620-02 Section 7.5 |
8 | 涂层耐柔韧性 | AAMA 620-02 Section 7.6 ASTM D4145 |
9 | 耐落沙磨耗 | AAMA 620-02 Section 7.7 ASTM D968 |
10 | 耐盐酸(15 mins,10%HCl) | AAMA 620-02 Section 7.8.1 |
11 | 耐泥浆(24h, 100% RH,38°C) | AAMA 620-02 Section 7.8.2 |
12 | 耐硝酸(30 mins) | AAMA 620-02 Section 7.8.3 |
13 | 耐清洁剂 (72h, 38°C) | AAMA 620-02 Section 7.8.4 |
14 | 耐湿(3000h,100% RH,38°C) | AAMA 620-02 Section 7.9.1 ASTM D2247-02 or ASTM D4585-07 |
15 | 耐盐雾 (3000h) | AAMA 620-02 Section 7.9.2 ASTM B117-07a |
16 | 耐候测试 (南佛罗里达州,北纬27度,45度角面向南方,5年曝晒) | AAMA 620-02 Section 7.10 |
颜色保持力 | AAMA 620-02 Section 7.10.1.2 ASTM D2244 Section 6.3 | |
耐粉化性 | AAMA 620-02 Section 7.10.1.3 ASTM D4214 | |
光泽度保持力 | AAMA 620-02 Section 7.10.1.4 ASTM D523 | |
耐侵蚀 | AAMA 620-02 Section 7.10.1.5 ASTM B244 | |
建筑用铝表面阳极氧化膜质量标志规定 | ||
条款 | 测试要求 | 测试标准 |
2.1 | 外观 | Qualicoat |
2.2 | 光泽度 | ISO 2813-94 |
2.3 | 涂层厚度 | ISO 2360:2003 |
2.4 | 附着力 | ISO 2409-2007 |
2.5 | (巴克霍尔兹)压痕试验 | ISO 2815-2003 |
2.6 | 杯突试验 | ISO1520-2006 |
2.7 | 抗弯曲性试验(漆膜弯曲强度) | ISO1519-2002 |
2.8 | 耐冲击性 | ASTM D2794-93(2004) |
2.9 | 耐二氧化硫潮湿空气试验(24 cycles) | ISO 3231 ISO 4628-2 |
2.10 | 耐酸性盐雾试验(1000h) | ISO 9227-2006 ISO 4628-2 |
2.11 | 马丘试验(加速腐蚀试验,只对型材) | Qualicoat |
2.12 | 加速风化试验(1000h) | ISO 11341:2004 |
光泽变化 | ISO 2813-94 | |
色差 | ISO 7724-3:1984 | |
2.13 | 自然气候测试 | ISO 2810 |
光泽变化 | ISO 2813-94 | |
色差 | ISO 7724-3:1984 | |
2.14 | 聚合测试 | Qualicoat |
2.15 | 耐灰浆试验 | ASTM C207/ASTM D3260 |
2.16 | 耐沸水试验(2h) | Qualicoat |
2.17 | 耐冷凝水测试(1000h) | DIN 50017 |
起泡程度判定 | ISO 4628-2 | |
2.18 | 抗锯,铣,钻测试 | Qualicoat |